| Diamension Of Protection Tubes | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Material | Diameter Size | Characteristics | ||||||||||
| SUS 304 | mm. Ø 4.8 , 6.3 , 8 , 9.5 , 12.7 , 15.8 , 19 , 20 | Up to 900°C (1650°F) under oxidizing conditions. Has generally good oxidation and corrosion resistance in a wide range of industrial invironments. Good mechanical properties from - 185 to 790°C (-300 to 1450°F) Main areas of usage : chemicals, food, plastics, petroleum. | ||||||||||
| SUS 316L | mm. Ø 3 , 3.2 , 4 , 4.8 , 6 , 6.3 , 8 , 9.5 , 10 , 12 , 14 , 15 , 15.8 , 18 , 21.3 | Up to 930°C (1700°F) under oxidizing conditions. Same area of application as 304 plus improved resisitance to acids and pitting corrosion | ||||||||||
| SUS 310S | mm. Ø 15.8 , 21.3 | Up to 1050°C (2100°F) under oxidizing conditions. Has high elevated temperature strength and scale resistance. Power plant boiler tubes to 980°C (1800°F) are the main areas of application. | ||||||||||
| SUS 466 | mm. Ø 21.3 | Up to 1090°C (2000°F) under oxidizing conditions. Excellent hight temperature corrosion and oxidation resistance. Main areas of application are: hardening; nitriding and annealing furnaces; salt baths and molten lead; tin and babbitt metal; sulphurous atmospheres. Not suitable for carburizing atmospheres. Other areas are: steel soaking pits; tining pots; waste heat boilers; ore roasters; cement exit flues; boiler tubes to 980°C(1800°F); asphalt mixing; incinerators to 1090°C(2000°F); glass tank flues | ||||||||||
| Inconel 600 | mm. Ø 10 , 21.3 | Up to 1260°C (2300°F) under oxidizing conditions. For reducing conditions, lower maximum temperature to 1040°C(1900°F). SOme resistance to sulphurous atmospheres. Main areas of application; carburizing, annealing and hardening furnaces; cyanide salt baths; blast furnace downcomers; steel soaking pits; waste heat boilers; ore roasters; cement exit flues; incinerators; glass tank flues. Do not use in vacuum furnaces. Susceptible to intergranular attack by prolonged heating in ther temperature range 540 - 760°C (1100 - 1400°F) | ||||||||||